AMS-T-21014
AMS-T-21014 |
Class 1 |
Class 1 |
Class 2 |
Class 2 |
Composition |
90W7Ni3Fe |
91W6Ni3Fe |
92W5Ni3Fe |
93W4Ni3Fe |
Density (g/cm3) |
17.1±0.15 |
17.25±0.15 |
17.50±0.15 |
17.60±0.15 |
Heat Treatment |
Sintering |
Sintering |
Sintering |
Sintering |
Tensile Strength (MPa) |
900-1000 |
900-1000 |
900-1100 |
900-1100 |
Elongation (%) |
18-29 |
17-27 |
16-26 |
16-24 |
Hardness(HRC) |
24-28 |
25-29 |
25-29 |
26-30 |
AMS-T-21014 |
Class 3 |
Class 3 |
Class 4 |
Composition |
95W3Ni2Fe |
96W3Ni1Fe |
97W2Ni1Fe |
Density (g/cm3) |
18.10±0.15 |
18.30±0.15 |
18.50±0.15 |
Heat Treatment |
Sintering |
Sintering |
Sintering |
Tensile Strength (MPa) |
920-1100 |
920-1100 |
920-1100 |
Elongation (%) |
10-22 |
8-20 |
6-13 |
Hardness(HRC) |
27-32 |
28-34 |
28-36 |
Desuden kan vi fremstille wolfram tunge legerede produkter som pendant til 90WNIMOFE produkter. Egenskaber for 90WNIMOFE produkter er blevet vist som følger:
90WNIMOFE
Products |
Normal Composition |
Density(g/cm3) |
UTS(N/mm2) |
Hardness (HRC) |
Applications |
| 90WNIMOFE |
90%W4Mo4Ni2Fe |
17.25 |
965 |
34 |
|
93WNIMOFE |
93%WNiFeMo |
17.8 |
885 |
30 |
Extrusion Dies |
90-WNIMOFE |
90%WNiFeMo |
17.3 |
960 |
32 |
Die Casting Tools, Extrusion Tools |
86WNIMOFE |
86%WNiFeMo |
16.7 |
1075 |
36 |
Die Casting Tools |
Typical Properties of 90WNIMOFE
Chemistry: |
90%W, 4%Ni; 4%Mo; 2%Fe |
Density: |
0.62lb/in3 |
17.25g/cm3 |
Hardness: |
34HRC |
67HRA |
Ultimate Tensile Strength: |
140ksi |
965Mpa |
RT Yield Strength (.2%) |
125ksi |
862Mpa |
RT Elongation (in 2’’) |
3% |
|